2014 | 2013 | 2012 | 2011 | 2010 | 2009 | 2008 | 2007 | 2006 | 2005 | 2004 | 2003 | 2002 | 2001 | 2000 | 1999 | 1998 | 1997 | 1996 | 1995 | 1994 | 1993 | 1992 | 1991 | 1990 | 1989 | 1988 | 1987 | 1986 | 1985 | 1984 | 1983 | 1982 | 1981 | 1980 | 1979 | 1978 | 1977 | 1976 | 1975 | 1974 | 1973 | 1972 | 1971 | 1970 | 1969 | 1968 | 1967 | 1966 | 1965 | 1964 | 1963 | 1962 | 1961 | 500 | 76 | 0

Electric properties of single-phased BiFeO3 ceramics

Authors: Miao, JH; Xiao, JZ; Xu, L; Paixao, JA ; Costa, MMR; Costa, B; Hugo, V; Shi, FN

Ref.: Ferroelectrics 452, 57-62 (2013)

Abstract: Densed BiFeO3(BFO) ceramics were sintered by using soft chemical derived fine powders. The microstructures, polarization and dielectric properties were investigated by means of X-rays diffraction (XRD), Scanning electron microscope (SEM), ferroelectric test system and impedance analyzer. The XRD patterns indicate that BFO ceramics with a single distorted perovskite structure are formed and no secondary phase appears in the ceramics. Through the dielectric response investigated over a wide range of temperature and frequency, it is found that the BFO ceramic sintered at 800 degrees C exhibited high dielectric permittivity and two dielectric relaxations. The remanent polarization and maximum polarizations were 0.232 and 0.443C/cm(2), respectively (at 25kV/cm).

DOI: 10.1080/00150193.2013.841489