2014 | 2013 | 2012 | 2011 | 2010 | 2009 | 2008 | 2007 | 2006 | 2005 | 2004 | 2003 | 2002 | 2001 | 2000 | 1999 | 1998 | 1997 | 1996 | 1995 | 1994 | 1993 | 1992 | 1991 | 1990 | 1989 | 1988 | 1987 | 1986 | 1985 | 1984 | 1983 | 1982 | 1981 | 1980 | 1979 | 1978 | 1977 | 1976 | 1975 | 1974 | 1973 | 1972 | 1971 | 1970 | 1969 | 1968 | 1967 | 1966 | 1965 | 1964 | 1963 | 1962 | 1961 | 500 | 76 | 0
Developmentof High Curie Temperature Ferroelectric xBi(Sc0.5Yb0.5)O3 – (1-x)PbTiO3 syngle crystals
Authors: L. Xu, J. Xiao, J.A. Paixão, B.F.O. Costa, M.M.R. Costa,
Ref.: Ferroelectrics 447 (2013)
Abstract: Bismuth based ferroelectrics xBi(Sc0.5,Yb0.5)O3–(1-x)PbTiO3 (BYSPT) solid-solution systems had been anticipated to hold a high Curie temperature (Tc), meeting the conditions for using under high-temperature environment. In the current research, a solid state reaction processing route had been adopted to synthesize BYSPT based ceramics, and developed BYSPT crystals by a flux approach. The as-grown BYSPT perovskite crystals exhibit a Tc of about 570°C, based on measurements of dielectric and thermal properties.