2014 | 2013 | 2012 | 2011 | 2010 | 2009 | 2008 | 2007 | 2006 | 2005 | 2004 | 2003 | 2002 | 2001 | 2000 | 1999 | 1998 | 1997 | 1996 | 1995 | 1994 | 1993 | 1992 | 1991 | 1990 | 1989 | 1988 | 1987 | 1986 | 1985 | 1984 | 1983 | 1982 | 1981 | 1980 | 1979 | 1978 | 1977 | 1976 | 1975 | 1974 | 1973 | 1972 | 1971 | 1970 | 1969 | 1968 | 1967 | 1966 | 1965 | 1964 | 1963 | 1962 | 1961 | 500 | 76 | 0
Chitosan-silica composite aerogel for the adsorption of cupric ions
Authors: João P. Vareda, Pedro M. C. Matias, José A. Paixão, Dina Murtinho, Artur J. M. Valente, Luisa Durães
Ref.: Gels 10(3), 192(1)-16 (2024)
Abstract: A chitosan-silica hybrid aerogel was synthesized and presented as a potential adsorbent for the purification of cupric ion-contaminated media. The combination of the organic polymer (chitosan), which can be obtained from fishery wastes, with silica produced a mostly macroporous material with an average pore diameter of 33 mu m. The obtained aerogel was extremely light (56 kg m-3), porous (96% porosity, 17 cm3 g-1 pore volume), and presented a Brunauer-Emmett-Teller surface area (SBET) of 2.05 m2 g-1. The effects of solution pH, aerogel and Cu(II) concentration, contact time, and counterion on cupric removal with the aerogel were studied. Results showed that the initial pH of the cation-containing aqueous solution had very little influence on the removal performance of this aerogel. According to Langmuir isotherm, this material can remove a maximum amount of ca. 40 mg of cupric ions per gram and the kinetic data showed that the surface reaction was the rate-limiting step and equilibrium was quickly reached (in less than one hour). Thus, the approach developed in this study enabled the recovery of waste for the preparation of a novel material, which can be efficiently reused in a new application, namely water remediation.