2014 | 2013 | 2012 | 2011 | 2010 | 2009 | 2008 | 2007 | 2006 | 2005 | 2004 | 2003 | 2002 | 2001 | 2000 | 1999 | 1998 | 1997 | 1996 | 1995 | 1994 | 1993 | 1992 | 1991 | 1990 | 1989 | 1988 | 1987 | 1986 | 1985 | 1984 | 1983 | 1982 | 1981 | 1980 | 1979 | 1978 | 1977 | 1976 | 1975 | 1974 | 1973 | 1972 | 1971 | 1970 | 1969 | 1968 | 1967 | 1966 | 1965 | 1964 | 1963 | 1962 | 1961 | 500 | 76 | 0
Magnetic Studies on New Mixed-Valence Phosphates Zn2+Fe23+(P2O7)(2) and Zn0.52+Cu0.52+Fe23+(P2O7)(2)
Authors: Lamsaf, H; Oulmekki, A; Elghadraoui, EH; Fausto, R; Wagner, FE; Costa, BFO
Ref.: J. Supercon. Nov. Magn. 32(5), 1377-1382 (2019)
Abstract: Structural studies of Zn2+Fe3+2(P2O7)2 and Cu0.5Zn0.5Fe2(P2O7)2 were made using powder X-ray diffraction and refined by Rietveld method. Both phosphates crystallize in an orthorhombic structure with Pnma space group. Magnetometry measurements showed that below TN = 5.6 (1), Zn2+Fe3+2(P2O7)2 becomes antiferromagnetic and the TN = 14 K is attributed to Cu0.5Zn0.5Fe2(P2O7)2. Mossbauer studies at room temperature and low temperature were performed in both samples.