2014 | 2013 | 2012 | 2011 | 2010 | 2009 | 2008 | 2007 | 2006 | 2005 | 2004 | 2003 | 2002 | 2001 | 2000 | 1999 | 1998 | 1997 | 1996 | 1995 | 1994 | 1993 | 1992 | 1991 | 1990 | 1989 | 1988 | 1987 | 1986 | 1985 | 1984 | 1983 | 1982 | 1981 | 1980 | 1979 | 1978 | 1977 | 1976 | 1975 | 1974 | 1973 | 1972 | 1971 | 1970 | 1969 | 1968 | 1967 | 1966 | 1965 | 1964 | 1963 | 1962 | 1961 | 500 | 76 | 0
Ball milling in vacuum of alpha and sigma phases of near-equiatomic FeCr alloys
Authors: B.F.O. Costa, G. Le Caër and J.M. Loureiro
Ref.: Journal of Alloys and Compds 483, 70-73 (2009)
Abstract: The structural changes induced by ball-milling of near-equiatomic sigma-FeCr and alpha-FeCr in vacuum were followed. Besides the a-phase, an amorphous phase appears when milling the sigma-phase for times longer than 20 h. An amorphous phase forms too, but at a slower rate than the latter, when milling the alpha-phase. The partial amorphisation of sigma-FeCr and alpha-FeCr ball-milled in vacuum is concluded to be a phenomenon of intrinsic origin. The amorphous phase crystallizes into a bcc Cr-rich phase and a bcc Fe-rich phase during short annealing steps. (C) 2008 Elsevier B.V. All rights reserved.