2014 | 2013 | 2012 | 2011 | 2010 | 2009 | 2008 | 2007 | 2006 | 2005 | 2004 | 2003 | 2002 | 2001 | 2000 | 1999 | 1998 | 1997 | 1996 | 1995 | 1994 | 1993 | 1992 | 1991 | 1990 | 1989 | 1988 | 1987 | 1986 | 1985 | 1984 | 1983 | 1982 | 1981 | 1980 | 1979 | 1978 | 1977 | 1976 | 1975 | 1974 | 1973 | 1972 | 1971 | 1970 | 1969 | 1968 | 1967 | 1966 | 1965 | 1964 | 1963 | 1962 | 1961 | 500 | 76 | 0
Design and development a novel uranyl sensor based on FePt/ZnIn2S4 core-shell semiconductor nanostructures
Authors: Zeynali, H; Motaghedifard, M; Costa, BFO Akbari, H; Moghadam, Z; Babaeianfar, M; Rashidi, MJ
Ref.: Arab. J. Chem. 13(1), 1429-1439 (2020)
Abstract: In this study, the FePt core, ZnIn2S4 shell and FePt-ZnIn2S4 core-shell nanostructures were successfully synthesized using solvothermal process. Temperature dependent hysteresis behavior of as-synthesized nanoparticles (NPs) FePt and FePt/ZnIn2S4 showed super paramagnetic response at 300 K and ferromagnetic properties with a coercive field (Hc) of 2830 Oe and 970 Oe at 2 K, respectively. Also, the blocking temperature (TB) estimating by the peak in ZFC curves was about 26 K for FePt and about 46 K for FePt/ZnIn2S4 NPs. After the identification process of nanostructure, using electrochemical methods, the behavior of FePt-ZnIn2S4 core-shell@PGE was studied in 0.1 M phosphate buffer solution (PBS) containing 5.0 mM [Fe(CN)6]3�/4� . The EIS complex plane plots showed a drastic change in the charge transfer resistance of the probe redox reaction as a function of UO2 2+ concentration. This behavior was used for construction of the calibration curve, and a linear range from 0.5 to 10.0 lM UO2 2+ with a detection limit of 71.7 nM.