2014 | 2013 | 2012 | 2011 | 2010 | 2009 | 2008 | 2007 | 2006 | 2005 | 2004 | 2003 | 2002 | 2001 | 2000 | 1999 | 1998 | 1997 | 1996 | 1995 | 1994 | 1993 | 1992 | 1991 | 1990 | 1989 | 1988 | 1987 | 1986 | 1985 | 1984 | 1983 | 1982 | 1981 | 1980 | 1979 | 1978 | 1977 | 1976 | 1975 | 1974 | 1973 | 1972 | 1971 | 1970 | 1969 | 1968 | 1967 | 1966 | 1965 | 1964 | 1963 | 1962 | 1961 | 500 | 76 | 0
Effect of combined Ca/Ti and Ca/Nb substitution on the crystal and magnetic structure of BiFeO3
Authors: V.A. Khomchenko; D.V. Karpinsky; M.S. Ivanov; A. Franz; S.V. Dubkov; M.V. Silibin; J.A. Paixão
Ref.: J. Magn. Magn. Mater. 491, 165561 (2019)
Abstract: Herein, we report on the crystal structure, magnetic and local ferroelectric properties of the Bi1−xCaxFe1−xTixO3 and Bi1−xCaxFe1−x/2Nbx/2O3 perovskites prepared by a solid state reaction method. It has been found that the Ca2+/Nb5+-containing series is characterized by a narrower concentration range (x ≤ 0.2) over which the acentric R3c structure specific to the pure BiFeO3 can be stabilized. The compositional variation in the critical concentration defining the polar/nonpolar (R3c/Pnma) phase boundary can be understood as related to the chemical modification-induced changes in the lattice spacing diminishing the stability of the a−a−a− tilting in favor of the a−b+a− one. Both the Ca2+/Ti4+ and Ca2+/Nb5+ substitutions ensure the suppression of a cycloidal antiferromagnetic order, thus leading to the formation of a weak ferromagnetic polar state. While this effect is proven to be associated with a composition-driven reduction in polar displacements, lattice defects are supposed to contribute to the instability of the cycloidal spin arrangement.